Abstract:
In the osmotic power generation field, reaching the industrial benchmark has been challenging because of the need for capillaries close to the sizes of ions and molecules [1,2]. Here, we fabricate well-controlled “along-the-capillary” membranes of 2D Navermiculite with nanochannel sizes of ∼ 5 Å. They exhibit 1,600 times enhanced conductivity compared with commonly studied “across-the-capillary” membranes [3,4]. Interestingly, they show a very high cation selectivity of 0.83 for NaCl solutions, which results in large power densities of 9.6 W/m2 and 12.2 W/m2 at concentration gradients of 50 and 1,000, respectively, at 296 K, for a large membrane length of 100 μm. The power density shows an exponential increase with temperature, reaching 65.1 W/m2 for a concentration gradient of 50 at 333 K. This markedly differs from the classical behaviour and indicates the role of ion (de)hydration in enhancing power density, opening possibilities for exploiting other membranes made of 2D materials for energy harvesting applications.